Причина та профілактика тріщин у дуплексних кастингах з нержавіючої сталі Ce3MN

The research institution focused on the CE3MN casting super duplex stainless steel material for the valve body of the 30 "-300 Lb upper mounted ball valve. Using FactSage 8.2 thermodynamic calculation software and FSstel steel database, combined with experimental methods such as optical microscope, scanning electron microscope, energy dispersive spectrometer, and X-ray diffractometer, the cause of cracks in the Кастинг Матеріалів CE3MN Коли вирізали та проаналізовано обробку розчину AS перед розчином. matrix in the form of short rod like or fine needle like structures, or distributed at the α/γ phase boundary in the form of long chain like, strip like, coral like, (σ+γ 2) cell like, and long needle like Weibull structure. Production practice has shown that before gas cutting the riser of CE3MN castings, the blank is pre treated with solid solution treatment to eliminate the brittle σ phase in the as cast state, suppress crack formation and Розповсюдження або холодна пиляння використовуються для вирізання підстриженого підйомника перед обробкою твердого розчину, що може принципово уникнути температурного коефіцієнта, який викликає тріщини.